Ten pairs of thawed fresh-frozen human cadaveric lower arm specimens were subjected to lateral three-point bending. Either the radius or ulna were impacted with a 4.5 kg dropped weight at approximately 3 m/s or tested quasi-statically in a materials testing machine. Fracture occurred primarily near the loading site with an average dynamic peak load of 1370 N and average peak moment of 89 Nm. Differences between the radius and ulna were not significant. Static fracture load and moments were approximately 20% lower. Sectional and mineral properties of each specimen near the fracture sites were measured.