Biomimetic Scaffolds for Ligament Tissue Engineering

Links

URL: http://hdl.handle.net/1974/6952

Abstract

The primary objective of my thesis was to investigate the effect of crimp-like fibrous scaffolds on bovine fibroblasts and to develop a scaffold for anterior cruciate ligament (ACL) tissue engineering. To achieve this objective, fibrous biodegradable polymeric scaffolds were fabricated, which upon relaxation developed a crimp-like structure, which resembled the crimp seen in native collagen. The understanding of the crimp mechanism allowed for controlling crimp-like patterns in various polymer fibre systems, and was determined to be due to residual stress coupled with an operating temperature (Top) above the glass transition temperature of the polymer (Tg). The benefit of crimp was evaluated by seeding fibroblasts on crimp-like fibres that were subjected to dynamic mechanical loading. The results showed a significant increase in extracellular matrix (ECM) accumulation by fibroblasts that experienced crimp unfolding. In addition, fibroblasts seeded on mechanically stimulated crimp-like fibrous scaffolds formed ECM bundles that resembled collagen fibre fascicles.

Two separate studies were conducted to fabricate fibrous scaffolds with high modulus: one on thermoplastic polyesters and the other on a photocrosslinkable polyester. Of the thermoplastic polyesters investigated, poly(L-lactide-co-D,L-lactide) P(LLA-DLLA) exhibited the highest modulus, and was the most resistant to hydrolytic degradation. These fibres were placed in a heated aqueous environment to exhibit a crimp-like pattern similar to that of native collagen. Bovine fibroblasts were shown to attach, proliferate and deposit ECM on the surface of the P(LLA-DLLA) fibrous scaffolds. In addition, the deposited ECM appeared to be organized in distinctive bundles that resembled fascicles found in native ACL. However, upon crimp unfolding the crimp was not completely recovered. Photocrosslinkable poly(L-lactide-co-trimethylene carbonate cinnamate) P(LLA-TMC cinnamate) fibres in addition to supporting cell proliferation and ECM accumulation, completely recovered their crimp-like pattern, via [2 + 2] cycloaddition of the cinnamate groups. The recovery of crimp upon unfolding is a novel design feature incorporated into electrospun fibres as it innately mimics the function of collagen fibres found in the ACL.

From the results obtained it is evident that crimp and its unfolding are key design features/conditioning techniques that need to be incorporated into fibrous scaffolds that possess high modulus, intended for ligament tissue engineering.

Cited Works (16)

Year	Entry
2000	Temenoff JS, Mikos AG. Review: tissue engineering for regeneration of articular cartilage. Biomaterials. March 1, 2000;21(5):431-440.
1976	Crowninshield RD, Pope MH. The strength and failure characteristics of rat medial collateral ligaments. J Trauma. February 1976;16(2):99-105.
2006	Hayami J. Development of a Biomimetic Scaffold for Ligament Tissue Engineering [Master's thesis]. Queen's University; November 2006.
1976	Noyes FR, Grood ES. The strength of the anterior cruciate ligament in humans and Rhesus monkeys. J Bone Joint Surg. 1976;58A(8):1074-1082.
2003	Lynch HA, Johannessen W, Wu JP, Jawa A, Elliott DM. Effect of fiber orientation and strain rate on the nonlinear uniaxial tensile material properties of tendon. J Biomech Eng. October 2003;125(5):726-731.
2000	Butler DL, Goldstein SA, Guilak F. Functional tissue engineering: the role of biomechanics. J Biomech Eng. December 2000;122(6):570-575.
1999	Pioletti DP, Rakotomanana LR, Leyvraz P-F. Strain rate effect on the mechanical behavior of the anterior cruciate ligament–bone complex. Med Eng Phys. March 1999;21(2):95-100.
1993	Danto MI, Woo SL. The mechanical properties of skeletally mature rabbit anterior cruciate ligament and patellar tendon over a range of strain rates. J Orthop Res. January 1993;11(1):58-67.
1986	Farndale RW, Buttle DJ, Barrett AJ. Improved quantitation and discrimination of sulphated glycosaminoglycans by use of dimethylmethylene blue. Biochim Biophys Acta. September 4, 1986;883(2):173-177.
2002	Arnoczky SP, Lavagnino M, Whallon JH, Hoonjan A. In situ cell nucleus deformation in tendons under tensile load: a morphological analysis using confocal laser microscopy. J Orthop Res. January 2002;20(1):29-35.
2003	Waldman SD, Spiteri CG, Grynpas MD, Pilliar RM, Hong J, Kandel RA. Effect of biomechanical conditioning on cartilaginous tissue formation in vitro. J Bone Joint Surg. 2003;85A(suppl 2):101-105.
1992	Hynes RO. Integrins: versatility, modulation, and signaling in cell adhesion. Cell. April 3, 1992;69(1):11-25.
1988	Kim Y-J, Sah RLY, Doong J-YH, Grodzinsky AJ. Fluorometric assay of DNA in cartilage explants using Hoechst 33258. Anal Ciochem. October 1988;174(1):168-176.
1993	Langer R, Vacanti JP. Tissue engineering. Science. May 14, 1993;260(5110):920-926.
1998	Fratzl P, Misof K, Zizak I, Rapp G, Amenitsch H, Bernstorff S. Fibrillar structure and mechanical properties of collagen. J Struct Biol. 1998;122(1-2):119-122.
2007	Ilagan BG. The Development of an Elastomeric Scaffold for Small Diameter Blood Vessel Tissue Engineering [Master's thesis]. Queen's University; November 2007.