Influence of the fixation technique on the mechanical properties of human cancellous bone of the femoral head

Fischer, Benjamin; Hofmann, Alexander; Kurz, Sascha; Edel, Melanie; Zajonz, Dirk Jörg; Roth, Andreas; Schleifenbaum, Stefan

Affiliations

¹ZESBO – Center for Research on Musculoskeletal Systems, Leipzig University, Semmelweisstrasse 14, D-04103 Leipzig, Germany

²Department of Orthopaedic Surgery, Traumatology and Plastic Surgery, University of Leipzig Medical Center, Liebigstrasse 20, D-04103 Leipzig, Germany

Abstract

Background: The femoral head is of central importance for the force transmission from the suprapelvic body mass to the lower extremity. However, the condition of the subcortical bone and its mechanical properties in case of pathological changes due to coxarthrosis or femoral head necrosis differ from the healthy condition.

Methods: Fresh femoral heads were gathered during hip total endoprosthesis surgeries and cylindrical cancellous bone samples were extracted with a hollow drill. By means of a uniaxial tensile-compression test system, the compressive strength was determined for two different specimen types (fresh and 24 h storage in acetone). Exemplary tests on an exceptionally large femoral head were performed to compare properties of fresh, fresh-deep-frozen and acetone-stored samples.

Findings: The deformation behaviour and the material parameters determined were very heterogeneous. For most of the specimens, a destructive material test was successfully carried out, i.e. the compressive strength was determined. The average strength of fresh specimens was slightly higher than that of acetone specimens. On the other hand, the average Young's modulus of the acetone specimens was higher than that of the fresh specimens.

Interpretation: The lower Young's moodulus of the fresh samples compared to the acetone samples could indicate a causal effect of the degreasing influence of the acetone. The partly considerable individual differences in compressive strength and failure compression can have patient-specific influencing factors such as constitution and physical fitness as well as causes in the initial pathological condition.

Links

DOI: 10.1016/j.clinbiomech.2021.105280

PubMed: 33582564

WoS: 000632689900003

History

Received: 2019-12-20

Revised: 2021-01-19

Accepted: 2021-01-19

Online: 2021-01-24

Cited Works (5)

Year	Entry
2002	Brown SJ, Pollintine P, Powell DE, Davie MW, Sharp CA. Regional differences in mechanical and material properties of femoral head cancellous bone in health and osteoarthritis. Calcif Tiss Int. September 2002;71(3):227-234.
1974	Schoenfeld CM, Lautenschlager EP, Meyer PR. Mechanical properties of human cancellous bone in the femoral head. Med Biol Eng. 1974;12(3):313-317.
2012	Kefalas V, Eftaxiopoulos DA. Experimental study of cancellous bone under large strains and a constitutive probabilistic model. J Mech Behav Biomed Mater. February 2012;6:41-52.
2016	Torres AM, Matheny JB, Keaveny TM, Taylor D, Rimnac CM, Hernandez CJ. Material heterogeneity in cancellous bone promotes deformation recovery after mechanical failure. Proc Natl Acad Sci USA. March 15, 2016;113(11):2892-2897.
1994	Keaveny TM, Guo XE, Wachtel EF, McMahon TA, Hayes WC. Trabecular bone exhibits fully linear elastic behavior and yields at low strains. J Biomech. 1994;27(9):1127-1136.