Characterization of Hydroxyapatite Whisker Reinforced Composites and Scaffolds for Mechanical and Biological Function in Orthopaedic and Spinal Implants

Links

URL: https://curate.nd.edu/show/5q47rn31z9h

Abstract

The overall objective of this study was to investigate the mechanical and biological properties of HA whisker reinforced polyaryletherketone (PAEK) composites and scaffolds which are key to clinical translation for orthopedic and spinal implants. The fatigue behavior of polyetherketoneketone (PEKK) reinforced with 0, 20, and 40 vol% hydroxyapatite (HA) was investigated in four-point bending fatigue. The fatigue life decreased with increasing HA reinforcement. However, PEKK reinforced with 40 vol% HA whiskers exhibited a fatigue life greater than 2⋅10⁶ cycles at 40 MPa. Moreover, HA whisker reinforcement resulted in decreased creep deformation and minimal modulus degradation.

The effects of the mold temperature and polyetheretherketone (PEEK) powder were investigated on the mechanical properties and crystallinity of HA whisker reinforced PEEK scaffolds prepared using compression molding and porogen leaching. The mechanical properties of the scaffolds increased while the PEEK crystallinity decreased, with increasing mold temperature and suggested an optimal mold temperature of 370-375°C for PEEK scaffolds comprising of 75% porosity and 20 vol% HA whisker reinforcement, regardless of the PEEK powder size.

The effects of the porogen morphology on the architecture, mechanical properties, and permeability of HA whisker reinforced PEEK scaffolds were investigated in 75 – 90% porous scaffolds. HA whisker reinforced PEEK scaffolds prepared with an ellipsoidal porogen exhibited a greater permeability than scaffolds prepared with a cubic porogen. The compressive modulus, yield strength, and yield strain were not affected by the porogen morphology.

The effects of HA reinforcement morphology and content was investigated on the behavior of primary osteoblasts on dense HA reinforced PEEK substrates in vitro. At day 7, the number of osteoblasts attached to PEEK substrate surfaces increased with increasing HA content and for HA whiskers compared to equiaxed HA powder reinforcement. This suggests that the HA reinforcement content morphology can promote cellular attachment and proliferation at early time points.

Cited Works (11)

Year	Entry
2005	Van Nausdle JA. Effects of Hydroxyapatite Morphology on MC3T3-E1 Osteoblast-Like Cells [Master's thesis]. University of Notre Dame; October 2005.
1999	Turner CH, Rho J, Takano Y, Tsui TY, Pharr GM. The elastic properties of trabecular and cortical bone tissues are similar: results from two microscopic measurement techniques. J Biomech. April 1999;32(4):437-441.
1998	Rho J-Y, Kuhn-Spearing L, Zioupos P. Mechanical properties and the hierarchical structure of bone. Med Eng Phys. 1998;20(2):92-102.
2006	Rezwan K, Chen QZ, Blaker JJ, Boccaccini AR. Biodegradable and bioactive porous polymer/inorganic composite scaffolds for bone tissue engineering. Biomaterials. June 2006;27(18):3413-3431.
1997	Odgaard A. Three-dimensional methods for quantification of cancellous bone architecture. Bone. 1997;20(4):315-328.
2005	Karageorgiou V, Kaplan D. Porosity of 3D biomaterial scaffolds and osteogenesis. Biomaterials. September 2005;26(27):5474-5491.
1989	Sasaki N, Matsushima N, Ikawa T, Yamamura H, Fukuda A. Orientation of bone mineral and its role in the anisotropic mechanical properties of bone: transverse anisotropy. J Biomech. 1989;22(2):157-164.
2006	Rogel MR. Effects of Hydroxyapatite Crystal Morphology on Osteoblast-Like Cell Response [Master's thesis]. University of Notre Dame; July 2006.
2002	LeGeros RZ. Properties of osteoconductive biomaterials: calcium phosphates. Clin Orthop Relat Res. February 2002;395:81-98.
2001	Keaveny TM, Morgan EF, Niebur GL, Yeh OC. Biomechanics of trabecular bone. Annu Rev Biomed Eng. 2001;3:307-333.
1999	Hildebrand T, Laib A, Müller R, Dequeker J, Rüegsegger P. Direct three-dimensional morphometric analysis of human cancellous bone: microstructural data from spine, femur, iliac crest, and calcaneus. J Bone Miner Res. July 1999;14(7):1167-1174.