Hypertension is a major predisposing factor to initiate thoracic aortopathy. The objective of this study is to investigate effect of hypertension on delamination and tensile strength of ascending thoracic aortic aneurysms (ATAAs). A total of 35 fresh ATAA samples were harvested from 19 hypertensive and 16 non-hypertensive patients during elective aortic surgery. Peeling tests with two extension rates were performed to determine delamination strength, while uniaxial tensile (UT) tests were employed to measure failure stresses. The delamination strength and failure stresses of the ATAAs were further correlated with patient ages for hypertensive and non-hypertensive groups. The delamination strength to peel apart the ATAA tissue along the longitudinal direction was statistically significantly lower for the hypertensive patients than that of the non-hypertensive patients (35 ± 11 vs. 49 ± 9 mN/mm, p = 0.02). A higher delamination strength was measured if peeling was performed with a higher extension rate. The circumferential failure stresses were significantly lower for the hypertensive ATAAs than those of the non-hypertensive ATAAs (1.03 ± 0.27 vs. 1.43 ± 0.38 MPa, p = 0.02). Histology showed that laminar structures of elastic fibers were mainly disrupted in the hypertensive ATAAs. The longitudinal delamination strength of the ATAAs was significantly decreased and strongly correlated with ages for the hypertensive patients. Strong inverse correlations were also identified between the circumferential and longitudinal failure stresses of the ATAAs and ages for the hypertensive patients. Results suggest that the ATAAs of the elderly hypertensive patients may have a higher propensity for dissection or rupture. The dissection properties of the ATAA tissue are rate dependent.