Aponeuroses are stiff sheath-like components of the muscle-tendon unit that play a vital role in force transmission and thus locomotion. There is clear importance of the aponeurosis in musculoskeletal function, but there have been relatively few studies of aponeurosis material properties to date. The goals of this work were to:​ 1) perform tensile stress-relaxation tests, 2) perform planar biaxial tests, 3) employ computational modeling to the data from 1 to 2, and 4) perform scanning electron microscopy to determine collagen fibril organization for aponeurosis tissue. Viscoelastic modeling and statistical analysis of stress-relaxation data showed that while relaxation rate differed statistically between strain levels (p ¼ 0.044), functionally the relaxation behavior was nearly the same. Biaxial testing and associated modeling highlighted the nonlinear (toe region of ~2–3% strain) and anisotropic (longitudinal direction linear modulus ~50 MPa, transverse ~2.5 MPa) tensile mechanical behavior of aponeurosis tissue. Comparisons of various constitutive formulations showed that a transversely isotropic Ogden approach balanced strong fitting (goodness of fit 0.984) with a limited number of parameters (five), while damage modeling parameters were also provided. Scanning electron microscopy showed a composite structure of highly aligned, partially wavy collagen fibrils with more random collagen cables for aponeurosis microstructure. Future work to expand microstructural analysis and use these data to inform computational modeling would benefit this work and the field.